#1
July 9th, 2014, 01:44 PM
| |||
| |||
Model question papers of TANCET Textile technology exam
Can you give me question paper for Tamil Nadu common entrance test Textile technology examination ??
|
#2
July 9th, 2014, 04:08 PM
| |||
| |||
Re: Model question papers of TANCET Textile technology exam
Here I am giving you question paper for Tamil Nadu common entrance test Textile technology examination in PDF file attached with it so you can get it easily 76. The tensile strength of polynosic fibre is around 1. 3 to 3.5 gmsldenier 3. to gmsldenier 77. In viscose solution preparation xanthation process takes normally from 1. 10 minutes 60 to 180 minutes 3. 5 hours 4. 24 hours 78. The temperature of molten polymer in nylon 81. 82. The tenacity range of acrylic fibre in gmsldenier is 1. to 1.2 The modern false twist texturizing machines can impart false twist in to moving yarn a t the rate of 1. six million RPM 2. 1 2 million RPM 3. only 30,000 RPM 4. RPM only 66 manufacture is around 79. In acrylic fibre manufacture, the polymer concentration ranges from 83. High bulk yarns are produced from 1. relaxed fibres 2. unrelaxed fibres 3. a blend of relaxed and unrelaxed fibres filaments 84. The cord fabrics used in conveying belt applications approximately weigh 4. 70 to 8 0 % 80. The work factor of viscose staple fibre is around 85. The cotton cloth construction normally applied in V-belts in and is 86. The standard parachute cloth in 1. 2 to 3 2. 7 to 10 3. 25 to 30 4. 50 to 100 strength of nylon width is 91. Knitted fabric width is expressed as 1. Total number of needles x wales per inch 2. Total number of needles wales per inch 3. Total number of needles - wales per inch 87. The number of twistslmetre involved in high stretch yarns is around 1. 100 2. 2500 3. 500 4. 250 88. An unbalanced structure in weft knitting process is 1. Polka rib 2. Royal rib 3. Eight lock 4. Derby rib 89. In Jacquard knitting the maximum design width of intermediate Jacquard is 1. 48 wales 2. 24 wales 3. 144 wales 4. 182 wales 4. Wales per inch Total no. of needles 92. According to law which of the following relations is correct in weft knitting? where S = Stitch density is constant = Stitch length 93. In purl knitting machine the two needle beds are set a t 1. 2. 3. 90. The normal cut of the non-Jacquard knitting machine is around 1. 24 2. 48 3. 72 4. 88 94. -320From tricot knitting machine the fabric comes off the machine a t an angle of 2. 3. 95. The width of Raschel machines varies from 1. 480 to 600 cm 2. 200 to 350 cm 3. to 1500 cm 150 t o 200 cm 96. In the dielectric phenomenon of fibres water is considered to be 1. Induced dipole 2. Permanent dipole 3. Temporary dipole 4. An ordinary molecule 97. The percentage amorphous region in wool fibre is around 98. Higher the bi-refringence of a fibre 1. higher will be the orientation 2. lower will be the orientation 3. higher will be the amorphous portions 4. higher will be the crystallinity 99. The optical orientation factor of an isotropic fibre is 101. The best synthetic fibre for good elastic recovery is 1. Polyester 2. Nylon 3. Acrylic 4. Polypropylene 102. The % absorption moisture regain of nylon 6.6 at 65% R.H. and 20°C is 1. 4.1 2. 2.1 3. 8.0 4. 0.4 103. The chemical potential of a solute in an ideal solution may be expressed as 104. The reactive dyeing process for 100 % cotton garment involves duration of dyeing as 1. 1 to 2 hours 2. 2 to hours 3. 3 to 4 hours 4. 5 to 6 hours 105. The interfibrillary swelling takes place in 1. water solution acid and strong alkali solution 3. water and weak alkali solution 4. alkali solution 100. With increase in relative humidity, the 106. The heat of for cotton fibre is strength of wool fibre 1. increases 2. decreases 3. first increases and then decreases 4. does not change 1. 17.9 107. The simple test for mercerization of cotton is 1. Examining under sunlight 2. Examining under U.V. light 3. Examining through microscope 4. Examining through infra-red light 108. The cross-section of cotton fibre changes due 111. The top roller of two bowl calender used for calendering process is made of 1. hard plastic 2. hard steel 3. soft paper 4. wood 112. Which one of the following fibres is not used to mercerization from 1. Flat shape to oval shape 2. Bean shape to round shape 3. Round shape to elliptical shape 4. Elliptical shape to bean shape for the production of 1. Viscose rayon 2. Glass 3. Polyester 4. Silk cord? 109. The removal of sericine results in a weight 113. The stelometer is made of CRL system by 1. step synchronous motor loss of silk by 2. damping device 1. 40 to 75 % 2. 70 to 90 % 3. 2 0 t o 2 5 % 110. The california bearing ratio resistance in textiles is expressed as 1. CBR resistance = failure load cross- sectional area 2. CBR resistance = cross-sectional area 3. cam drive 4. beam design 114. For 3 % trash in mixing the cleaning efficiency expected in is 1. 65 % 2. 35 % 3. 80 % 4. 25 % I n single yarn tensile strength test, higher failure load 1. lower the strength will result 3. CBR resistance = failure load x cross- sectional area 4. CBR resistance = cross-sectional area - failure load 2. no change in strength '3. higher the strength 4. no change in extension |
|